| Specification | : | PART A EPOXY 1 KG : RESIN |
|---|---|---|
| Appearance Liquid | : | Clear |
| Specific gravity @ 25°C | : | 1.05 |
| Viscosity @ 25°C, poises | : | 11000-12000 |
| Colour | : | Clear |
| Amine value by HCIO4 method Mg of KOH/gm | : | 450 |
| Mixing Ratio: Epoxy Compound:Resins:Hardener:Filler | : | 1000:500:3000 |
| Working Timing | : | 25°C for min 25 minutes |
| Hardener after 8 hrs. | : | Shore D-40 |
| Tensile Strength Kgs/cm2 | : | 250-300Kgs/cm2 - 90MPA |
| Compressive Strength | : | Min 600Kgs/cm2 - 0.48 GPA |
| Hardener's Specification | ||
| Solids | : | 95 Min |
| Viscosity (cPs, @ 25 deg C) | : | 500 ~ 1500 |
| Colour | : | Orange-Brown |
| Amine Value (mg KOH/g) | : | 360-420 |
| Density (g/ml@25 deg C) | : | 0.99 ~ 1.05 |
| AHEW | : | 95 |
| Flash Point (deg C) | : | >104 |
| Gel Time (mins, 100gm @ 25 deg C) | : | 20-30 |
| PHR* 0 for EEW-190 | : | 50±5 |
| Deg C | : | 3-4hrs. |
| Fully Cured | : | 7 Days |
| Cross hatch | : | 5B |
| Pencil Hardness | : | <4H |
| Chemicals Resistance | : | Resist to mild acid and base Poor resistance to solvent |
| Compressive Strength (mPas.) | : | >60 mPass |
| SILICA SAND PART C 3Kgs | ||
| Product Identifier | : | Silica Sand, Filter Sand |
| Other means of Identification | : | Quartz, Crystalline Silica, Silica Dioxide, Ground Silica |
| Product use and Restrictions on use | : | Use for Epoxy Compound |
| Specification | : | PART A EPOXY 1 KG : RESIN |
|---|---|---|
| Appearance Liquid | : | Clear |
| Specific gravity @ 25°C | : | 1.05 |
| Viscosity @ 25°C, poises | : | 11000-12000 |
| Colour | : | Clear |
| Amine value by HCIO4 method Mg of KOH/gm | : | 450 |
| Mixing Ratio: Epoxy Compound:Resins:Hardener:Filler | : | 1000:500:3000 |
| Working Timing | : | 25°C for min 25 minutes |
| Hardener after 8 hrs. | : | Shore D-40 |
| Tensile Strength Kgs/cm2 | : | 250-300Kgs/cm2 - 90MPA |
| Compressive Strength | : | Min 600Kgs/cm2 - 0.48 GPA |
| Hardener's Specification | ||
| Solids | : | 95 Min |
| Viscosity (cPs, @ 25 deg C) | : | 500 ~ 1500 |
| Colour | : | Orange-Brown |
| Amine Value (mg KOH/g) | : | 360-420 |
| Density (g/ml@25 deg C) | : | 0.99 ~ 1.05 |
| AHEW | : | 95 |
| Flash Point (deg C) | : | >104 |
| Gel Time (mins, 100gm @ 25 deg C) | : | 20-30 |
| PHR* 0 for EEW-190 | : | 50±5 |
| Deg C | : | 3-4hrs. |
| Fully Cured | : | 7 Days |
| Cross hatch | : | 5B |
| Pencil Hardness | : | <4H |
| Chemicals Resistance | : | Resist to mild acid and base Poor resistance to solvent |
| Compressive Strength (mPas.) | : | >60 mPass |
| SILICA SAND PART C 3Kgs | ||
| Product Identifier | : | Silica Sand, Filter Sand |
| Other means of Identification | : | Quartz, Crystalline Silica, Silica Dioxide, Ground Silica |
| Product use and Restrictions on use | : | Use for Epoxy Compound |
Hardener is soluble in aromatic hydrocarbons, higher alcohols, ketones and insoluble in aliphatic hydrocarbons and water. Grouting materials are selected based on the type of load they will support. Dynamic loads are associated with reciprocating equipment, motors, generators, turbines etc. Static loads are associated with columns or non-moving equipment. Epoxy grouts offer unique performance advantages in many applications. They achieve strength quickly, allowing fast return to service or commissioning of equipment. Greater bond to the underside of a prepped baseplate, density and lower modulus of elasticity help to absorb impact and vibration. Low shrinkage and high tensile and flexural strengths optimize load transfer ensuring stable, secure alignment and protecting equipment from unnecessary wear and tear. Chemical resistance properties ensure they are durable even in harsh industrial environments. With more than 25 years of experience in precision equipment grouting, HANDA CHEM is an early developer and pioneer in both cementitious and epoxy grouts. We understand not only the in-service performance demands that our grouts must meet, but also the inter-relationship between various physical properties and application criteria that must be carefully considered. Handa Chem has applied advanced chemistry to balance the physical properties of compressive strength, bearing area, chemical and high temperature resistance, shrinkage and creep with the sometimes difficult yet also very important application enablers of flow and working time, to provide uncompromised and durable support, protecting the equipment investment by improving reliability, operating efficiency and life cycle of machinery. The performance of any epoxy grout, in fact for most all construction materials, depends on the proper fit-for-purpose design, and the proper installation. This Guide to Epoxy Grouting is designed to help equipment manufacturers, engineers and specifiers, owners and contractors understand the Proper Preparation, Mixing, Installation & Testing of Epoxy Grouts to enable durable, quality, installations of Grouts.
Hardener is compatible with all grades of modified and unmodified liquid Resins and Epoxy compound the curing is dependent on the hardener system and temperature for technical department of the company.
Parts by Weight
This 3 pack is specially made for Road safety
| Product Code: Epoxy Resin and Hardener + Filler for Road Safety Products | ||
|---|---|---|
| Specification | : | After Mixing 3 Parts |
| Appearance Liquid of 3 Pack after mixing | : | Off white |
| Specific gravity @ 25°C | : | 1.35 |
| Viscosity @ 25°C, poises | : | 12000-15000 |
| Colour | : | Off White |
| Amine value by HCIO4 method Mg of KOH/gm | : | 450 |
| Mixing Ratio 1:0.5:3KG | : | Hardener 50% of Epoxy Resin |
| (a) 1KG Resin (b) 500Gm Hardener (c) 3Kg Filler | ||
| Pot Life of 140gm | : | 8 to 10 minutes |
| Mixing Ratio | : | Epoxy 1Kg, Filler 3Kg, Hardener 500gm |
| Tensile Strength Kgs/cm2 | : | 90MPA |
| Compressive Strength | : | 0.48 GPA |
Hardener is soluble in aromatic hydrocarbons, higher alcohols, and ketones and insoluble in aliphatic hydrocarbons and water.
Parts by Weight
Hardener is compatible with all grades of modified and unmodified liquid Resins and Epoxy compound the curing is dependent on the hardener system and tempreature for technical department of the company.